The The Effect of Ultrasonic activation on the Microstructure and Phase Transformation of Porous Ni-Ti Shape Memory Alloys
DOI:
https://doi.org/10.22353/physics.v36i605.9334Keywords:
Microstructure, Phase transformation, Ultrasonic, Ni-Ti alloyAbstract
Porous Ni-Ti shape memory alloys (SMAs) have been widely studied in Biomaterial for biomedical applications because they have a porous structure similar to human bone and corrosion resistance. A porous Ni-Ti SMAs was obtained by self-propagating high-temperature synthesis (SHS) and investigated its microstructure and phase transformation. This article presents the results of a study of changes in the microstructure and phase transformation of porous Ni-Ti SMAs when Ni and Ti metal powders were preliminarily subjected to ultrasonic activation at different amplitude (5-25μm). The results show that the microstructure of porous Ni-Ti SMAs consists of Ni-Ti matrix and Ni-Ti2 precipitates. Two-step phase transformation was observed in porous Ni-Ti alloys.
Downloads
References
K. Otsuka, and X. Ren. Intermetallics. 1999, 7, 511. doi.org/10.1016/S0966-9795(98)00070-3.
Sahar A.Fadlalah, Nader El-Bagoury, Sanaa M.F.Gad El-Rab, Rasha A.Ahmed, Ghaida El-Ousamii. J Alloys and Compd. 2014, 583, 455.
N. Resnina, S. Belyaev, A. Voronkov. J Mater Eng Perfor. 2018, 27, 1257. https://doi.org/10.1007/S11665-018-3231-Z.
G. Tosun, G, L. Ozle. J Alloys and Compd. 2009, 487, 605. https://doi.org/10.1016/j.jallcom.2009.08.023.
G. Tosun, N. Orhan, L. Ozler, L, Mater Lett, 2012, 66, 138. https://doi.org/10.1016/j.matlet.2011.08.023.
Javaherian, S.S., Aghajani, H. & Mehdizadeh, P. Int. J Self-Propag. High-Temp. Synth. 2014, 23, 47. https://doi.org/10.3103/S1061386214010051
B. Y. Li, L. J. Rong, Y. Y. Li, V. E. Gjunter. Acta Mater. 2000, 48, 3895. https://doi.org/10.1016/S1359-6454(00)00184-1.
W. Sirikul, D. Nipon, S. Lek. Mater. Sci. Eng. A. 2009, 515, 93. DOI: 10.1016/j.msea.2009.02.055
C. A. Biffi, P. Bassani, Z. Sajedi, P. Giuliani, A. Tuissi. Mater. Lett. 2017, 193, 54. https://doi.org/10.1016/j.matlet.2017.01.097.
M. Kaya, N. Orhan, B. Kurt, T. Khan,. J Alloys and Compd. 2009, 475, 378. https://doi.org/10.1016/j.jallcom.2008.07.023
R.R Chen, D.H Zheng, et all.. Scientific reports. 2017, 7, 41463. doi: 10.1038/srep41463.
P. Snopinski, T. Donie, et all.. Materials. 2021, 14, 1010. https://doi.org/10.3390/ma14041010
N. Resnina, V.V. Rubanik Jr.V.V. Rubanik, S. Belyaev, V. Bysha, V. Kalganov, D. Chepela,. Letter on Mater. 2022, 12, 164. https://doi.org/10.22226/2410-3535-2022-2-164-168
M. Dovchinvanchig, P. Enkhtsetseg, V.V. Rubanik Jr.V.V. Rubanik. Materials , 2023, 16,6134.https://doi.org/10.3390/ma16186134
A. Saadati, H. Aghajani. J Mater Sci. 2019, 30, 92. DOI: 10.1007/s10856-019-6296-9
Jian, Y.T.; Yang, Y.; Tian, T.; Stanford, C,; Zhang, X.P,; Zhao, Ke.. PLOS one. 2015, 11, 0149051. DOI: 10.1371/journal.pone.0128138
Kaya, M, Çakmak, Ö. Metall Mater Trans A. 2016, 47, 1499. https://doi.org/10.1007/s11661-015-3318-1.
M.Kilic, B.Yenigun, S.Bati, Batman, Z.Balalan and I. Kirik. Materi Testing 2019, 61, 1140. DOI: 10.3139/120.111439
P.Bassani, S.Panseri, A.Ruffini, M.Montesi, M. Ghetti, C.Zanotti, A.Tampieri, A.Tuissi. J Mater Sci Mater Med. 2014, 25, 2277. doi: 10.1007/s10856-014-5253-x
Resnina, N.; S. Belayev, S.; Voronkov, A. Intermatellics. 2013, 32, 81. https://doi.org/10.1016/j.intermet.2012.08.009
Downloads
Published
How to Cite
Issue
Section
Categories
License
Copyright (c) 2024 Scientific transaction of the National University of Mongolia. Physics
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.